316L Stainless Steel Coil

Product Detail

If you are going to buy high quality 316l stainless steel coil in stock, please feel free to contact Sheye Metal, which is one of the well-known manufacturers and suppliers of good 316l stainless steel coil.

Brief Description of 316L Stainless Steel Coil

AISI 316L stainless steel coils are inventoried in 0.3mm to 16mm thickness and 1000mm to 2500mm width. Wider width is also available according to customer’s requirement. 316L 2B stainless steel coils and 316L BA stainless steel coils are the most common products in Sheye Metal. We always stock them for more than 2000 Tons.

316L stainless steel, also named as 1.4404 stainless steel, is an austenitic stainless steel which belongs to Cr-Ni-Mo stainless steel family. Low carbon content for 316L grade stainless steel makes it show better resistance against intergranular corrosion after welding. 316L stainless steel coils can be used in applications with increased demand for corrosion resistance because of its molybdenum content. The typical applications of 316L stainless steel coil includes equipment in the chemical and petrochemical industry, pulp and paper industry equipment, textile industry equipment, food and beverage industry equipment, pharmaceutical industry equipment, medical applications.


Specification of 316L Stainless Steel Coil
Size	Cold Rolled: Thickness: 0.3 ~ 8.0mm; Width:1000 ~   2000mm
	Hot Rolled: Thickness: 3.0 ~ 16.0mm; Width:1000 ~   2500mm
Techniques	Cold Rolled, Hot Rolled
Surface	2B, BA, 8K, 6K, Mirror Finished, No.1, No.2,   No.3, No.4, Hair Line with PVC
Cold Rolled 304   Stainless Steel Coil in Stock	316L 2B Stainless Steel Coil 316L BA Stainless Steel Coil
Hot Rolled 304   Stainless Steel Coil in Stock	316L No.1 Stainless Steel Coil
Common Sizes   of 304 Stainless Steel Sheet	1000mm x 2000mm, 1200mm x 2400mm, 1219mm x   2438mm, 1220mm x 2440mm, 1500mm x 3000mm, 1500mm x 6000mm, 1524mm x 3048mm,   2000mm x 6000mm
Protective   Film for 304 Stainless Steel Coil (25µm ~ 200µm)	White and Black PVC film; Blue PE film,   Transparent PE film, Other color or material are also available.
Standard	ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T   8165, BS 1449, DIN17460, DIN 17441, EN10088-2

 

The Common Thickness of Cold Rolled 316L Stainless Steel Coil
0.3mm	0.4mm	0.5mm	0.6mm	0.7mm	0.8mm	0.9mm	1.0mm	1.2mm	1.5mm
1.8mm	2.0mm	2.5mm	2.8mm	3.0mm	4.0mm	5.0mm	6.0mm

 

The Common Thickness of Hot Rolled 316L Stainless Steel Coil
3.0mm	4.0mm	5.0mm	6.0mm	8.0mm	10.0mm	12.0mm	14.0mm	16.0mm

 

Chemical Composition of 316L Stainless Steel Coil
Element	AISI 304   / EN 1.4301
Carbon	=0.030
Manganese	=2.00
Sulfur	=0.030
Phosphorus	=0.045
Silicon	=0.75
Chromium	16.0~18.0
Nickel	10.0~14.0
Molybdenum	2.00~3.00
Nitrogen	=0.10




Mechanical Properties of 316L Stainless Steel Coil
Yield   Strength 0.2% offset (MPa)	Tension   Strength (MPa)	% Elongation   (2” or 50mm)	Hardness(HRB)
=170	=485	=40	=95




Processing Service of 316L Stainless Steel Coil
Stainless Steel Coil Surface Grinding	Polished Surface; Brushed Surface; Mirror Finish; Coated with PVC/PE film
Stainless Steel Coil Slitting & Cutting	Cutting to the specified weight; Cutting to the specified width
Stainless Steel Perforated Processing	Holes Diameter: 0.4mm ~ 120mm; Center to Center Distance: =1.4mm; Width of Coil/Sheet: =2000mm; Thickness: 0.3mm ~ 16mm; Holes Shape: Round, Square, Rectangular,   Triangular, Rhombus(Diamond), Oval, Hexagon, etc.

 

Fabrications of 316L Stainless Steel
Cold Forming   of 316L Stainless Steel	AISI316L / EN 1.4404 stainless steel can be   readily formed and processed using a full range of cold forming operations.   It can be used in heading, drawing, bending. Any cold forming operations will   increase the strength and hardness of the material.
Hardening of   316L Stainless Steel	AISI316L / EN 1.4404 stainless steel can be   hardened by heat treatment. However, it can be hardened by cold forming.
Hot Forming of   316L Stainless Steel	Hot forming can be carried out in the 850? ~ 1150? range. For   maximum corrosion resistance, forgings should be annealed at 1070? and   rapidly cooled in the air or water after hot forming operatins.
Annealing of   316L Stainless Steel	Quench annealing should be performed at 1030? to   1110? and followed by rapid cooling in water or air. In applications where   high residual stresses cannot be accepted, stress relief treatment may be   necessary.
Machining of   316L Stainless Steel	AISI316L / EN 1.4404 stainless steel is more   difficult to machine than ordinary carbon steels but are still comparatively   easier than more highly alloyed stainless grades. 316L stainless steel   requires higher cutting forces than carbon steels, and it shows resistance to   chip breaking, and a high tendency to built-up edge formation.
Welding of   316L Stainless Steel	AISI316L / EN 1.4404 stainless steel has   excellent weldability and it is suitable for the full range of conventional   welding methods, such as MMA, MIG, MAG, TIG, SAW, LBW, or RSW, except gas   welding. In order to fully restore the corrosion resistance of weld seam, the   weld discoloration should be removed by pickling and passivation.

 

Packing Information of 316L Stainless Steel Coils

AISI316L stainless steel coils from Sheye Metal are packed according to the customer’s requirement. To avoid any damage which might be caused during international transportation, we provide some optional packaging methods, including Kraft Water-proofing Paper, Plastic Bags, PVC Coated, Wooden Pallets.